生產(chǎn)的用丁基橡膠是一種用于中空玻璃的單組分、無(wú)溶劑、不霧化、不硫化和性塑料密封劑。

The produced butyl rubber is a single component, solvent-free, non atomizing, non vulcanizing, and permanent plastic sealant used for insulating glass.

熱熔丁基密封膠在較寬的溫度范圍內保持其塑性和密封性，表面不開(kāi)裂、不硬化。由于其極低的水蒸氣透過(guò)率，可與彈性密封膠一起形成優(yōu)良的防潮體系。

Hot melt butyl sealant maintains its plasticity and sealing properties over a wide temperature range, with no surface cracking or hardening. Due to its extremely low water vapor transmittance, it can form an excellent moisture-proof system together with elastic sealant.

因此密封效果好，質(zhì)量容易保證。不需要熟化期，節省了占地面積，降低了生產(chǎn)成本；它是一種產(chǎn)品，無(wú)廢棄物，環(huán)境清潔。

Therefore, the sealing effect is good and the quality is easy to ensure. No need for maturation period, saving land area and reducing production costs; It is an environmentally friendly product with no waste and a clean environment.

中空玻璃用丁基膠粘劑是雙組分聚氨酯密封膠、雙組分聚硫密封膠、雙組分硅酮密封膠和中空玻璃熱熔膠制作中空玻璃道密封的必備膠粘劑。根據中空玻璃丁基膠涂機膠倉的大小，選擇不同規格的中空玻璃丁基膠。

Butyl adhesive for insulating glass is an essential adhesive for the first sealing of insulating glass, which includes two-component polyurethane sealant, two-component polysulfide sealant, two-component silicone sealant, and insulating glass hot melt adhesive. Select different specifications of insulating glass butyl adhesive according to the size of the adhesive compartment of the insulating glass butyl adhesive coating machine.

用中空玻璃丁基橡膠制作中空玻璃時(shí)，應注意以下7點(diǎn):

When making insulating glass with butyl rubber, the following 7 points should be noted:

1.中空玻璃丁基橡膠-使用注意事項。清潔鋁隔條以備后用。

1. Hollow glass butyl rubber - Precautions for use. Clean the aluminum partition strip for future use.

2.將丁基熱熔密封膠放入擠出機料筒，預熱130-140℃。恒溫器保持恒溫后，在沖膠條檢查均勻性和連續性時(shí)，將膠條涂在鋁隔斷槽上，用干凈的玻璃壓住，稍冷卻后形成中空玻璃半成品。

2. Put the butyl hot melt sealant into the extruder barrel and preheat it to 130-140 ℃. After maintaining a constant temperature with the thermostat, when checking the uniformity and continuity of the adhesive strip, apply the strip to the aluminum partition groove, press it with clean glass, and cool it slightly to form a semi-finished hollow glass product.

3.外層密封膠涂覆固化后，即得到成品中空玻璃。

After the outer layer of sealant is coated and cured, the finished hollow glass is obtained.

4.使用進(jìn)口快膠機時(shí)，膠筒溫度應提高10-15℃，擠壓壓力應由150兆帕調整到170-200兆帕，以使膠條均勻生產(chǎn)。

When using an imported fast glue machine, the temperature of the rubber cylinder should be increased by 10-15 ℃, and the extrusion pressure should be adjusted from 150 megapascals to 170-200 megapascals to ensure uniform production of the rubber strip.

5.服用和使用丁基熱熔密封膠時(shí)，請清潔雙手。密封膠表面不應沾有灰塵、油和溶劑(如丙酮、汽油等)。).戴上不起毛的手套，涂抹。

5. When taking and using butyl hot melt sealant, please clean your hands. The surface of the sealant should not be contaminated with dust, oil, or solvents (such as acetone, gasoline, etc.) Wear lint free gloves and apply.

6.觸摸熱膠時(shí)要小心燒傷。接觸膠水的手套應干凈，沒(méi)有毛刺或其他容易粘在膠水上的污染物。

Be careful of burns when touching hot glue. Gloves that come into contact with glue should be clean and free of burrs or other contaminants that can easily stick to the glue.